基于YAG/Nd:YAG_Cr4+:YAG键合晶体的被动调Q亚纳秒激光器.pdf
《基于YAG/Nd:YAG_Cr4+:YAG键合晶体的被动调Q亚纳秒激光器.pdf》由会员分享,可在线阅读,更多相关《基于YAG/Nd:YAG_Cr4+:YAG键合晶体的被动调Q亚纳秒激光器.pdf(9页珍藏版)》请在咨信网上搜索。
1、全固态被动调Q 激光器有光束质量好、脉冲宽度窄、结构紧凑等特点,在雷达探测、工业制造等领域具有广泛应用前景。对YAG/Nd:YAG/Cr4+:YAG键合晶体被动调Q 激光器的输出特性进行了理论和实验研究,在泵浦光中心波长为808 nm、光斑直径为230 m、泵浦功率为6.72 W的泵浦条件下,获得了平均功率1.41 W、脉宽736 ps,重复频率8.46 kHz的调Q 激光输出。进一步研究表明,随着泵浦光焦点远离Nd:YAG端面,激光光斑的对称性下降;且泵浦光焦点离Nd:YAG端面的距离沿晶体轴向增大时,激光阈值呈上升趋势。关 键 词:激光技术;全固态;键合晶体;被动调Q;Cr4+:YAG中
2、图 分 类 号:TN248.1 文 献 标 识 码:A 文章编号:1007-5461(2023)04-00483-09Passively Qswitched subnanosecond laser based on YAG/Nd:YAG/Cr4+:YAG composite crystalTANG Jingling 1,2,QI Yue 1,2,BAI Zhenxu 1,2*,QI Yaoyao 1,2,DING Jie 1,2,YAN Bingzheng 1,2,WANG Yulei 1,2,LYU Zhiwei 1,2(1 Center for Advanced Laser Technol
3、ogy,Hebei University of Technology,Tianjin 300401,China;2 Hebei Key Laboratory of Advanced Laser Technology and Equipment,Tianjin 300401,China)AbstracAbstract t:Due to its excellent characteristics of good beam quality,narrow pulse width and compact structure,all-solid-state passively Q-switched las
4、ers have a wide application in radar detection,industrial manufacturing etc.Here,the output characteristics of passively Q-switched YAG/Nd:YAG/Cr4+:YAG laser are studied theoretically and experimentally.While being pumped by 808 nm laser with 230 m beam diameter and 6.72 W power,a Q-switched laser o
5、utput with an average power of 1.41 W and pulse width of 736 ps at the repetition rate of 8.46 kHz is obtained.Furthermore,it is shown that the symmetry DODOI I:10.3969/j.issn.1007-5461.2023.04.007基金项目:国家自然科学基金重大科研仪器研制项目(61927815)作者简介:唐敬玲(1995-),女,山东临沂人,研究生,主要从事全固态被动调Q激光器方面的研究。E-mail:导师简介:吕志伟(1961-)
6、,山东烟台人,博士,教授,博士生导师,主要从事高能量固体激光器及非线性光学方面的研究。E-mail:收稿日期:2021-05-08;修改日期:2021-11-10*通信作者。量 子 电 子 学 报40 卷of the laser beam decreases as the focus of the pump laser moves away from the Nd:YAG end face,and the laser threshold shows an upward trend when the distance between the focus of the pump laser and
7、 the Nd:YAG end face increases along the axis of the crystal.K Keyey wordswords:laser techniques;all-solid-state;composite crystal;passively Q-switched;Cr4+:YAG0 引 言全固态被动调Q激光器具有结构紧凑、体积小等优点,被广泛应用于激光点火13、精密加工4,5等领域。与传统可饱和吸收体(如染料片等)相比,Cr4+:YAG晶体具有基态吸收截面大(10-18 cm2)、散热性能好、损伤阈值高(500 MW/cm2)等优点,是一种在1 m波段理
8、想的被动Q开关材料610。目前,全固态被动调Q激光器已经广泛应用在科研、军事等领域,但严重的热效应却阻止了其性能进一步提高。将激光晶体与可饱和吸收体进行热键合处理,并在键合晶体两端直接镀膜构成平-平腔结构,不仅能够有效改善激光器的热效应问题1113,也能够进一步压缩腔长、减少腔内损耗,获得高效率、短脉冲的调Q激光输出1416。2017年,Li等14报道了一种YAG/Nd:YAG/Cr4+:YAG激光器,泵浦脉宽为1 ms时,获得了11个调Q脉冲的稳定输出,其脉冲能量为210 J、脉宽为1.7 ns。2016年,Dascalu等17利用键合晶体Nd:YAG/Cr4+:YAG,实现了独立的四光斑输
9、出,且光斑间距在毫米量级。本文研究了激光二极管(LD)端面泵浦的YAG/Nd:YAG/Cr4+:YAG被动调Q激光器的输出特性。在泵浦光中心波长为808 nm、光斑直径为230 m、泵浦功率为6.72 W的条件下,实现了脉冲宽度为736 ps、平均功率为1.41 W、重复频率为8.46 kHz的调Q激光输出。1 模拟分析为研究晶体键合方式对激光器输出特性的影响,首先利用LASCAD软件对单Nd:YAG晶体、以及三种不同键合方式的Nd:YAG激光器的输出特性进行建模分析,键合方式及晶体长度如表1所示,晶体的端面尺寸均设置为3 mm 3 mm。四种不同的谐振腔结构及其泵浦方式如图1(a)(d)所示
10、。表1 激光晶体尺寸表Table 1 Laser crystals lengthParameterCrystal length/mmComposite crystalNd:YAG7YAG/Nd:YAG2+5Nd:YAG/YAG5+2YAG/Nd:YAG/YAG1+5+1在仿真模型中,设置泵浦功率为90 W,泵浦光斑直径为400 m,腔长为晶体长度7 mm,输出镜反射率为70%时,仿真所得结果如表2所示。由表2可知,基于YAG/Nd:YAG的激光器,其光束质量因子M 2最小,这表明长的前端键合YAG晶体能够有效改善热效应对激光器的影响。分析可知,键合晶体能够有效提高激光晶体的散热能力,降低热效应
11、对激光器的影响。基于以上模拟分析,使用LASCAD软件模拟分析键合方式对晶体内部温度及热应力分布的影响。四种激光晶体内部的温度分布如图1(e)(h)所示,由图可知,键合晶体YAG/Nd:YAG的中心温度低于其他晶体的中心温度,且靠近泵浦光一侧的端面温度最低。因此,Nd:YAG晶体的入射前端键合YAG晶体能够有效减少晶体端面的形变量,提高泵浦光的利用率。四种激光晶体内部484第 4 期唐敬玲等:基于YAG/Nd:YAG/Cr4+:YAG键合晶体的被动调Q亚纳秒激光器的热应力分布如图1(i)(l)所示,由图可知,前端键合晶体能够有效缓解端面热应力问题,且能够有效降低热透镜效应对激光器的影响,避免出
12、现因晶体端面热应力过大而造成晶体破裂现象。表2 不同键合晶体对应的激光输出特性仿真结果Table 2 Simulation results of laser output characteristics corresponding to different composite crystalsOutput parameterThreshold/WOutput power/WThermal focal length/mmSpot radius/mBeam quality M 2Composite crystalNd:YAG3.015.0327.6956.601.19YAG/Nd:YAG3.174
13、.9233.9558.201.13Nd:YAG/YAG3.24.7829.8859.601.75YAG/Nd:YAG/YAG3.24.8334.4960.801.17图1(a)(d)激光晶体示意图;(e)(h)Pin=10.72 W,激光晶体温度分布切面图;(i)(l)Pin=10.72 W,激光晶体热应力分布切面图Fig.1(a)-(d)Schematic of laser crystal;(e)-(h)Pin=10.72 W,Schematic diagram of temperature distribution inside laser crystals;(i)-(l)Pin=10.7
14、2 W,Schematic diagram of thermal stress distribution of laser crystals将LASCAD模拟的YAG/Nd:YAG/Cr4+:YAG激光器仿真结果与已有的研究成果进行对比,对比结果如表3所示,从表中可知,短的腔长有利于激光器输出特性的提高。而在键合晶体两端直接镀膜构成平-平腔结构,在减小激光器尺寸的基础上,降低腔内损耗,从而可进一步提高激光器的输出特性。表3 YAG/Nd:YAG/Cr4+:YAG被动调Q激光器仿真结果与其他研究成果对比表Table 3 Comparison of simulation result of YAG
15、/Nd:YAG/Cr4+:YAG passively Qswitched lasers and other research resultsMeasured parameterCrystal size/mm3Cavity length/mmSingle pulse energy/JPulse width/nsM 2Composite crystalYAG/Nd:YAG/Cr4+:YAG33(2+5+2)96911.421.13YAG/Nd:YAG/Cr4+:YAG/YAG1633(1+7+1+1)1018.21.231.18YAG/Nd:YAG/Cr4+:YAG1433(2+5.5+1.5)2
16、5425.81.91.7485量 子 电 子 学 报40 卷2 实验装置及结果2.1 实验装置根据模拟仿真结构,对YAG/Nd:YAG/Cr4+:YAG键合晶体进行激光实验研究,实验装置以及采用的晶体分别如图2(a)和(b)所示。LD耦合输出光纤的纤芯直径为200 m,波长为808 nm,光纤耦合头的光斑放大倍率分别为1倍和2倍,实测泵浦光束腰直径0分别为230 m、530 m。YAG/Nd:YAG/Cr4+:YAG的尺寸为3 mm 3 mm (2+5+2)mm。泵浦光入射端(YAG端)镀有HR808 nm/HT1064 nm的膜层作为前腔镜,Cr4+:YAG端镀有R=40%1064 nm的反
17、射膜作为输出镜,Cr4+:YAG初始透过率为40%。晶体由铜热沉包裹,并以水冷方式进行冷却。2.2 实验结果及分析理论上,在相同泵浦功率情况下,泵浦光光斑口径越小,光斑处的光功率密度越大,所产生的激光阈值功率越低,但是入射光斑越小也会导致晶体内部热应力加剧。因此,选择合适的泵浦光半径0对获得稳定的激光输出具有重要意义。0分别在230 m和530 m两种情况下,测得输出光的平均功率Pout及脉冲宽度随注入泵浦功率Pin的变化关系如图3所示。由图3(a)可知,在相同泵浦功率情况下,0=530 m的激光产生阈值为0=230 m的四倍以上,一方面是由于泵浦功率密度下降,另一方面是泵浦光斑尺寸的增加影响
18、入射光与腔内振荡光的模式匹配,且入射光斑越大腔内模式竞争越严重。该实验结果与泵浦光直径对固体激光器和半导体激光器激光阈值的影响吻合18,19。此外,由图3(b)可看出,泵浦功率确定的情况下,输出激光的脉冲宽度与0正相关。0=230 m,Pin=6.72 W时,脉宽测得最小值736 ps;0=530 m,Pout=13.82 W时,脉宽测得最小值1300 ps。其主要原因是泵浦光功率密度减小,导致脉冲产生及饱和吸收体漂白的时间大幅增加;且随着泵浦功率的增加,调Q脉冲激光的脉宽呈先下降后上升的趋势。当0=230 m时,调Q激光的单脉冲时域波形随泵浦功率的变化如图4所示。在一定功率范围内,Pin的增
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- 基于YAG_Nd:YAG_Cr%5E%284 %29:YAG键合晶体的被动调Q亚纳秒激光器 基于 YAG_Nd YAG_Cr 284 29 YAG 晶体 被动 亚纳秒 激光器
1、咨信平台为文档C2C交易模式,即用户上传的文档直接被用户下载,收益归上传人(含作者)所有;本站仅是提供信息存储空间和展示预览,仅对用户上传内容的表现方式做保护处理,对上载内容不做任何修改或编辑。所展示的作品文档包括内容和图片全部来源于网络用户和作者上传投稿,我们不确定上传用户享有完全著作权,根据《信息网络传播权保护条例》,如果侵犯了您的版权、权益或隐私,请联系我们,核实后会尽快下架及时删除,并可随时和客服了解处理情况,尊重保护知识产权我们共同努力。
2、文档的总页数、文档格式和文档大小以系统显示为准(内容中显示的页数不一定正确),网站客服只以系统显示的页数、文件格式、文档大小作为仲裁依据,平台无法对文档的真实性、完整性、权威性、准确性、专业性及其观点立场做任何保证或承诺,下载前须认真查看,确认无误后再购买,务必慎重购买;若有违法违纪将进行移交司法处理,若涉侵权平台将进行基本处罚并下架。
3、本站所有内容均由用户上传,付费前请自行鉴别,如您付费,意味着您已接受本站规则且自行承担风险,本站不进行额外附加服务,虚拟产品一经售出概不退款(未进行购买下载可退充值款),文档一经付费(服务费)、不意味着购买了该文档的版权,仅供个人/单位学习、研究之用,不得用于商业用途,未经授权,严禁复制、发行、汇编、翻译或者网络传播等,侵权必究。
4、如你看到网页展示的文档有www.zixin.com.cn水印,是因预览和防盗链等技术需要对页面进行转换压缩成图而已,我们并不对上传的文档进行任何编辑或修改,文档下载后都不会有水印标识(原文档上传前个别存留的除外),下载后原文更清晰;试题试卷类文档,如果标题没有明确说明有答案则都视为没有答案,请知晓;PPT和DOC文档可被视为“模板”,允许上传人保留章节、目录结构的情况下删减部份的内容;PDF文档不管是原文档转换或图片扫描而得,本站不作要求视为允许,下载前自行私信或留言给上传者【自信****多点】。
5、本文档所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用;网站提供的党政主题相关内容(国旗、国徽、党徽--等)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。
6、文档遇到问题,请及时私信或留言给本站上传会员【自信****多点】,需本站解决可联系【 微信客服】、【 QQ客服】,若有其他问题请点击或扫码反馈【 服务填表】;文档侵犯商业秘密、侵犯著作权、侵犯人身权等,请点击“【 版权申诉】”(推荐),意见反馈和侵权处理邮箱:1219186828@qq.com;也可以拔打客服电话:4008-655-100;投诉/维权电话:4009-655-100。