注塑工艺培训讲座.pptx
《注塑工艺培训讲座.pptx》由会员分享,可在线阅读,更多相关《注塑工艺培训讲座.pptx(138页珍藏版)》请在咨信网上搜索。
1、1、塑料胶粒的软化和塑化(螺杆塑化过程)螺杆结构的设计必须保证得到均匀一致的熔体2、塑料熔体计量螺杆转速,背压3、塑料熔体向锁闭型腔注射锁模力比型腔压力高20%,熔体以均衡的方式充填模具型腔,以避免内应力的产生 多级注塑、充模流动行为、型腔压力分布、熔体PVT性质4、冷却熔体凝固并保持模具型腔形状 均匀的模具表面温度,避免制件翘曲、保证尺寸精度5、制件顶出塑化过程最大计量行程屏障螺杆关于塑料的特征分子量熔体指数PVT性质剪切稀化行为热稳定性收缩行为最大流动比吸湿性PVT性质材料的收缩特性温度引起的体积变化结晶高分子29%无定型高分子8%压力引起的体积变化10-15%Poly-merDensit
2、yRoomTemp.Processtemp.degreecDensityprocesstemp%ageinjectionutilisa-tioncapacityPermissibleresidencetime-min.Max-flowratiofor1mmwallthicknessScrewcushionmmShrinkage%OutputratiorelatedtoPsScrewrpmrelatedtoPsABS1.05220-2600.9640-80100-1404-60.4-0.70.830.83CA1.29170-2501.1050-805-830030.4-0.7NANAPOM1.4
3、2192-2151.1630-8015100-2302-62NANAPMMA1.18220-2601.0935-804-8100-1302-60.4-0.80.940.74PPO1.06250-290NA30-808100-1403-40.4-0.7NANAPA6/61.14220-2800.9540-805100-2302-4NA0.580.50PC1.22280-3101.0850-802-360-10040.7-0.80.670.57PES1.37330-400NANANA60-1204-50.60.950.83PBT1.31220-270NA40-803-4125-1854NANANA
4、PPS1.5-2.1300-360NA50-802-4120-1504-60.2NANAPETP1.38260-3001.250-802-450-9041.3-1.50.80.74PS1.05220-2700.9525-902-4150-20040.451.001.00HDPE0.95220-2800.7410-851702-61.5-20.730.94LDPE0.92180-2800.7410-952002-6NA0.821.05PP0.91250-2750.7310-8517041.2-2.20.630.86RPVC1.3-1.6170-190NA25-8020600.5-0.2NANAS
5、PVC1.1-1.14180-200NA20-801518041.2NANASAN1.08240-2700.9940-805-6140-18040.50.961.12TPU1.20180-225NA40-80305031-1.15NANA剪切变稀行为螺杆压缩区的剪切稀化喷嘴的剪切稀化热稳定性Kx最大射胶体停留时间=-x成型周期型腔体积注塑过程充模过程85-98%注塑行程切换过程压实过程冷却过程注塑过程中的收缩行为加工过程对收缩的影响不同材料的收缩率MATERIALS%SHRINKAGEMATERIALS%SHRINKAGENylon61-1.5Polycarbonate0.8Nylon6-GR
6、0.5Acetal2Nylon6/61-2PVC-Rigid0.5-0.7Nylon6/6-GR0.5PVC-Soft1-3LDPE1.5-3ABS0.4-0.6HDPE2-3PP1.2-2Polystyrene0.5-0.7Celluloseacetate0.5Styrene-acrylonitrile0.4-0.6Celluloseacetate.butyrate0.5Acrylic0.3-0.6Cellulosepropionate0.5收缩收缩与翘曲收缩与结晶收缩与加工过程收缩与取向收缩与冷却充模与冷却均衡流动调整均衡性调整均衡性与模具和机台相关的注塑缺陷缩痕壁厚设计不均匀可通过注塑压
7、力、保压压力、注塑速度调整尺寸变化冷却不均匀,调整保压压力、时间、强化冷却均匀性翘曲熔接缝降解重量变化POSITIONSPEEDPRESSUREFILLING PHASEAlso known as Speed phase.Selectendof1ststepandstartof2ndstep.SetSPEED1Trytosethigh.Only one pressure setting is required during FILLING PHASE.Pressure Setting should be more than actual filling pressure.as relief v
8、alve should not be actuated.If it is actuated,then speed control will be lost.Filling pressure depends on resistance to move the melt.It depends on flow ratio and viscosity of melt.Also known as Speed phase.There may be no.of steps available on machine.Selectendof2ndstepandstartof3rdstepSetSPEED2Low
9、erspeedforcrossingnarrowpassage/gateSteps are position controlled.Selectendof3rdstepandstartofSWITCHOVERPOINT.Thispointisataround80-95%oftheinjectionstroke.SetSPEED3Reducetolowersinkmark/increasetoshiftweldline.PRESSURE PHASE-Holding phase.There may be no.of steps available on machine.Timercontrolst
10、heHoldingpressurestepsifavailableonmachine.Holdingpressuretimeforstep1issetonatimer,Set SPEED low value say up to 35%not more.This can be one step of speed for different Holding steps.Speed set is low,as there is less or no space to move the melt.Holdingpressure1setjustenoughtofillcavitywithoutoverp
11、acking.Steps are timers controlled.Holdingpressuretimeforstep2issetonatimer,Holdingpressure2setjustenoughtofillcavitywithoutoverpacking.Holdingpressuretimeforstep3issetonatimer,Holdingpressure3setjustenoughtofillcavitywithoutoverpacking.均衡热交换均衡凝固熔接缝改变熔接缝位置成型周期The predominantly material causes involv
12、ed in failure were:The predominating process faults were:Environmental Stress Cracking,Excessive moulded-in stresses,Cyclic Fatigue,Voiding,Notch Sensitivity,Poor weld lines,Chemical Attack and;Stress Cracking,Adverse Orientation,UV Degradation,Material contamination,Thermal Degradation,Longer Resid
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- 注塑 工艺 培训 讲座 邹耀邦
1、咨信平台为文档C2C交易模式,即用户上传的文档直接被用户下载,收益归上传人(含作者)所有;本站仅是提供信息存储空间和展示预览,仅对用户上传内容的表现方式做保护处理,对上载内容不做任何修改或编辑。所展示的作品文档包括内容和图片全部来源于网络用户和作者上传投稿,我们不确定上传用户享有完全著作权,根据《信息网络传播权保护条例》,如果侵犯了您的版权、权益或隐私,请联系我们,核实后会尽快下架及时删除,并可随时和客服了解处理情况,尊重保护知识产权我们共同努力。
2、文档的总页数、文档格式和文档大小以系统显示为准(内容中显示的页数不一定正确),网站客服只以系统显示的页数、文件格式、文档大小作为仲裁依据,平台无法对文档的真实性、完整性、权威性、准确性、专业性及其观点立场做任何保证或承诺,下载前须认真查看,确认无误后再购买,务必慎重购买;若有违法违纪将进行移交司法处理,若涉侵权平台将进行基本处罚并下架。
3、本站所有内容均由用户上传,付费前请自行鉴别,如您付费,意味着您已接受本站规则且自行承担风险,本站不进行额外附加服务,虚拟产品一经售出概不退款(未进行购买下载可退充值款),文档一经付费(服务费)、不意味着购买了该文档的版权,仅供个人/单位学习、研究之用,不得用于商业用途,未经授权,严禁复制、发行、汇编、翻译或者网络传播等,侵权必究。
4、如你看到网页展示的文档有www.zixin.com.cn水印,是因预览和防盗链等技术需要对页面进行转换压缩成图而已,我们并不对上传的文档进行任何编辑或修改,文档下载后都不会有水印标识(原文档上传前个别存留的除外),下载后原文更清晰;试题试卷类文档,如果标题没有明确说明有答案则都视为没有答案,请知晓;PPT和DOC文档可被视为“模板”,允许上传人保留章节、目录结构的情况下删减部份的内容;PDF文档不管是原文档转换或图片扫描而得,本站不作要求视为允许,下载前自行私信或留言给上传者【天****】。
5、本文档所展示的图片、画像、字体、音乐的版权可能需版权方额外授权,请谨慎使用;网站提供的党政主题相关内容(国旗、国徽、党徽--等)目的在于配合国家政策宣传,仅限个人学习分享使用,禁止用于任何广告和商用目的。
6、文档遇到问题,请及时私信或留言给本站上传会员【天****】,需本站解决可联系【 微信客服】、【 QQ客服】,若有其他问题请点击或扫码反馈【 服务填表】;文档侵犯商业秘密、侵犯著作权、侵犯人身权等,请点击“【 版权申诉】”(推荐),意见反馈和侵权处理邮箱:1219186828@qq.com;也可以拔打客服电话:4008-655-100;投诉/维权电话:4009-655-100。